Articles of manufacture containing increased stability low concentration gases and methods of making and using the same

ABSTRACT

Articles of manufacture and methods of making and using same concern a container having an internal space and a passivated internal metal surface. The container contains a composition of an acid gas and a balance gas contained within the internal space and in contact with the passivated internal metal surface. The stability of the acid gas concentration over time is enhanced.

CROSS REFERENCE TO RELATED APPLICATIONS

This application claims priority from: copending provisional patent application Ser. No. 60/583,126, filed Jun. 25, 2004; copending non-provisional patent application Ser. No. 11/063,928, filed Feb. 22, 2005 which is a divisional of non-provisional patent application Ser. No. 10/157,468, filed May 29, 2005, now abandoned; and from non-provisional patent application Ser. No. 10/157,466, filed May 29, 2002, now published as U.S. 2003/0017359 A1, which claims priority to provisional patent application Ser. No. 60/306,014, filed Jul. 17, 2001, now abandoned. Each of these applications are incorporated by reference herein.

BACKGROUND OF THE INVENTION

Moisture is known to react with so-called “acid gases”, such as hydrogen sulfide, carbonylsulfide, carbondisulfide and mercaptans (mercaptans are also referred to as thiols) to form a complex compound. (The term “acid gas” is used herein to denote either gas phase, liquid phase, or mixture of gas and liquid phases, unless the phase is specifically mentioned.)

One problem presents itself: if one is interested in producing acid gas standard compositions, in other words acid gases having a known concentration of one of these gases in a matrix or carrier fluid, then one must consider how to reduce or remove the moisture. Gas standards may have to have, and preferably do have, a long shelf life, since the standard acid gas may not be required immediately after production. A source of acid gas and/or matrix gas may contain a considerable amount of moisture. Therefore, the reduction or removal of moisture from the acid gas is important if the stability of the acid gas in the standard gas is to be maintained.

U.S. Pat. Nos. 5,255,445 and 5,480,677 describe processes for drying and passivating a metal surface to enhance the stability of gas mixtures containing one or more gaseous hydrides in low concentrations in contact therewith. The process comprises purging gas in contact with the metal surface with inert gas to remove the purged gas, exposing the metal surface to an amount of a gaseous passivating or drying agent comprising an effective amount of a gaseous hydride of silicon, germanium, tin or lead and for a time sufficient to passivate the metal surface, and purging the gaseous passivating agent using inert gas. Optionally, an oxidizing agent is applied after the third step to stabilize the adsorbed stabilizing agent. The patent also mentions prior known processes, such as saturation passivation, where the container is subjected to several cycles of evacuating and filling with a much higher concentration of the same gaseous hydride, prior to being filled with the low concentration hydride mixture of interest. The two patents do not mention or describe processes to passivate containers adapted to store sulfur-containing gases, nor do they mention passivation techniques in which a first passivating agent is applied to the surface, followed by contacting with a higher concentration of the gas to be stored.

Co-pending application Ser. No. 10/157,467, filed on May 29, 2002 describes the use of certain acid gas resistant molecular sieves to reduce or remove moisture from fluid compositions comprising a sulfur-containing compound. There is no disclosure or suggestion, however, for the passivation of containers adapted to contain the moisture-reduced compositions. Such containers may have moisture adhered to the internal surfaces, which can and does react with acid gases, reducing their stability and shelf-life.

A second, related problem involves the containers that the reactive gas standards are stored in. If metal or metal lined, reactive gases will react with and/or become adsorbed onto the metal, and will ultimately change the concentration of the reactive gas.

Grossman et al. (U.S. Pat. No. 4,082,834) describes alloys, such as alloys of nickel, titanium, and zirconium, that react with water and reactive gases (such as hydrogen, hydrogen-containing compounds such as hydrocarbons, carbon monoxide, carbon dioxide, oxygen, and nitrogen) at temperatures ranging from about 200° C. to about 650° C. While the patent: does not discuss acid gases, it is apparent that hydrogen sulfide, carbonyl sulfide, and mercaptans are hydrogen-containing compounds, so that there would not be any expected benefits using these alloys to remove moisture from these acid gases. While carbondisulfide does not contain hydrogen, and therefore there could be some moisture reduction from a composition comprising carbondisulfide and moisture using these alloys, the high temperature is prohibitive for commercial use.

Tamhankar et al. (U.S. Pat. No. 4,713,224) describes a one-step process for removing minute quantities of impurities from inert gases, where the impurities are selected from the group consisting of carbon monoxide, carbon dioxide, oxygen, hydrogen, water and mixture thereof. The process comprises contacting the gas with a particulate material comprised of nickel in an amount of at least about 5% by weight as elemental nickel and having a large surface area, from about 100 to about 200 m²/g. There is no disclosure of removal of moisture from reactive gases; there is therefore no discussion or suggestion of moisture removal from reactive gases, moisture removal from matrix gases and mixing same to form a standard gas composition.

Tom et al (U.S. Pat. Nos. 4,853,148 and 4,925,646) discloses processes and compositions for drying of gaseous hydrogen halides of the formula HX, where X is selected from the group consisting of bromine, chlorine, fluorine, and iodine. The patent describes the use of, for example, an organometallic compound such as an alkylmagnesium compound, on a support. The halide is substituted for the alkyl functional group. Suitable supports are, alumina, silica, and aluminosilicates (natural or synthetic). However, there is no description or suggestion of reducing or removing moisture from sulfur-containing reactive gases, or of removal of moisture from matrix gases and mixing the reduced moisture gases to form a standard gas. Alvarez, Jr. et al. (U.S. Pat. No. 5,910,292) describes a process and apparatus for removal of water from corrosive halogen gases, using a high silica zeolite, preferably high silica mordenite. The patent describes removing moisture down to less than or equal to 100 ppb water concentration in halogen gases, particularly chlorine- or bromine-containing gases, but once again, there is lacking any teaching of suggestion of standard gas compositions. U.S. Pat. No. 6,183,539 discloses utilizing high sodium, low silica faujasite particles for the adsorption of carbon dioxide and water vapor from gas streams. The disclosed types of gas streams in which this type of high sodium, low silica faujasite crystals can be utilized includes air, nitrogen, hydrogen, natural gas, individual hydrocarbons and monomers, such as ethylene, propylene, 1,3 butadiene, isoprene and other such gas systems. There is no mention of sulfur-containing acid gas purification using the faujasites, or production of standard gas compositions.

U.S. Pat. No. 4,358,627 discloses use of “acid resistant” molecular sieves, such as that known under the trade designation “AW300”, for reducing the chloride concentration in chlorinated liquid hydrocarbons that contain an ethylenically unsaturated chlorinated hydrocarbon, water and hydrogen chloride. The method includes providing certain nitrogen-containing compounds in the system and contacting the system with the molecular sieve. There is no disclosure or suggestion, however, of removal or reduction of moisture from gas phase compositions, or production of standard gas compositions.

With respect to sulfur compounds, one impetus for measurement of low levels of these compounds has come from the hydrocarbon process industry where the requirement for lower sulfur measurements is steadily increasing. Controlling the concentration of sulfur is quite important for two major reasons. First, low sulfur content in simple olefin feed stock for high purity linear polymers such as polyethylene and polypropylene is quite important. Sulfur compounds adsorb onto the surface of the catalysts and prevent the desired reactants from reaching the catalytic surface thereby deactivating the catalyst. Given the quantity of these products produced annually, the economic impact can be quite significant. Therefore, common sulfur impurities in the feed stock, such as H₂S (hydrogen sulfide) and COS (carbonyl sulfide) must be carefully monitored.

Second, sulfur in the form of sulfur dioxide (SO₂), has been classified as a criteria pollutant by the EPA. This translates into strict regulation of emissions from coal burning plants, motor vehicle emissions, and paper and wood pulp processing plants to name a few. Sulfur in coal and gasoline becomes sulfur dioxide when the fuel is combusted. This SO₂ is a precursor to acid rain. Reducing sulfur in gas not only lowers sulfur dioxide emissions but also reduces catalytic converter poisoning. This increases a vehicle's pollution control efficiency thus reducing other pollutants.

In order to monitor, control and regulate these compounds and other reactive gases, calibration gas mixtures containing these compounds must be used. For these mixtures to be utilized successfully, they must be reliable with respect to stability (shelf life) and concentration. Significant challenges arise as the concentrations of reactive gas mixtures required to calibrate equipment are decreased. Interactions on the cylinder and tubing surfaces, such as chemical reactions and adsorption, are often insignificant with reactive gas concentrations in the range of 10 ppm and above. These interactions become quite important with reactive gases at concentrations at or below 1 ppm. Impurities, such as moisture, which are present in the source gas can also play a major role in the stability of these mixtures.

Given the problem of moisture reacting with acid gases and reactive gases in general, it would be advantageous if passivation methods could be provided which increase the shelf-life during the storage of these compounds.

SUMMARY OF THE INVENTION

In accordance with the present invention, articles of manufacture containing increased stability low concentration gases and methods of making and using the same are provided in order to enhance the stability of low concentration acid gas compositions within the articles over time.

A first aspect of the invention relates to an article of manufacture comprising:

-   -   a) a container having an internal space and a passivated         internal metal surface; and     -   b) a composition comprising an acid gas and a balance gas         contained within the internal space and in contact with the         passivated internal metal surface; wherein         -   i) the acid gas has a concentration in the balance gas of             less than 500 ppb;         -   ii) the acid gas is selected from the group consisting of             carbon disulfide, carbonylsulfide, and compounds within             formula (I):             Y—S—X  (I)         -    wherein S is sulfur, X and Y are the same or different and             are independently selected from the group consisting of             hydrogen, alkyl, aryl, oxygen, hydoxyl, amine, aminosilane,             oxygen, and alcohol; and         -   iii) the passivated internal metal surface comprises A) the             reaction product of a silicon-containing material and an             oxygen-containing material and B) the acid gas adsorbed on             or in the passivated internal metal surface in an amount             effective to enhance the stability of the intended             concentration over time.

A second aspect of the invention is a method of making an article of manufacture containing an acid gas having an intended concentration which is stably maintained over time, the method comprising the steps of:

-   -   exposing an internal metal surface of a container to a first         composition comprising one or more silicon-containing compounds         for a time sufficient to allow at least some of the         silicon-containing compound(s) to react with oxygen-containing         compounds present to form a silicon-treated surface on at least         some of the internal metal surface, the silicon-containing         compound(s) selected from the group consisting of compounds         within the general formula (II):         SiR¹R²R³R⁴  (II)         wherein R1, R2, R3, and R4 are the same or different and are         independently selected from the group consisting of hydrogen,         halogen, alkyl, aryl, amine, halogenated alkyl, and halogenated         aryl;     -   evacuating the container for a time sufficient to remove         substantially all of the silicon-containing compound(s) that has         not reacted with the oxygen-containing compound to form the         silicon-treated surface;     -   exposing the silicon-treated surface to a second composition         comprising an acid gas having a concentration that is greater         than an intended concentration of the acid gas;     -   evacuating the container for a time sufficient to remove an         amount of the second composition to enhance the stability of the         intended concentration over time; and     -   filling the container with a third composition comprising the         acid gas at the intended concentration.

A third aspect of the invention is a method of calibrating a measurement device for measuring a concentration of an acid gas, the method comprising the steps of:

-   -   providing a manufactured product comprising:         -   i) a container having an internal space and a passivated             internal metal surface; and         -   ii) a composition comprising an acid gas and a balance gas             contained within the internal space and in contact with the             passivated internal metal surface; wherein             -   A) the acid gas has an intended concentration of less                 than 500 ppb;             -   B) the acid gas is selected from the group consisting of                 carbon disulfide, carbonylsulfide, and compounds within                 formula (I):                 Y—S—X  (I)             -   wherein S is sulfur, X and Y are the same or different                 and are independently selected from the group consisting                 of hydrogen, alkyl, aryl, oxygen, hydoxyl, amine,                 aminosilane, oxygen, and alcohol; and             -   C) the passivated internal metal surface comprises 1)                 the reaction product of a silicon-containing material                 and an oxygen-containing material (preferably selected                 from the group consisting of moisture, molecular oxygen,                 metal oxides, and mixtures thereof), and 11) the acid                 gas adsorbed on or in the passivated internal metal                 surface in an amount effective to enhance the stability                 of the intended concentration over time; and     -   using a portion of the acid gas contained within the         manufactured product in a calibration of the measurement device;         and     -   repeating said step of using a portion at least once, wherein a         period of time commencing from a first performance of said step         of using a portion and expiring on a later repetition of said         step of using a portion is not less than 30 days.

Further aspects and advantages of the invention will become apparent by reviewing the description of preferred embodiments that follow.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 shows the stability of H₂S concentration in low-level H₂S standards over time;

FIG. 2 shows the stability of H₂S concentration in low-level H₂S standards over time;

FIG. 3 shows the stability of H₂S concentration in low-level H₂S standards over time;

FIG. 4 shows the stability of H₂S and COS concentrations in low-level H₂S and COS standards over time;

FIG. 5 shows the stability of SO₂ concentration in low-level SO₂ ndards over time;

FIG. 6 shows the stability of H₂S and COS concentrations in low-level H₂S and COS standards over time; and

FIG. 7 shows the stability of H₂S concentration in low-level H₂S standards over time.

DESCRIPTION OF PREFERRED EMBODIMENTS

While the following discussion focuses on a container which has a metal internal surface, the description is not limited thereto, and could apply to a piping or tubing system, a manifold, a gas cylinder having a cylinder valve, ton unit, and the like.

Initially, it is preferred to start with an abraded internal metal surface which has been vacuum baked prior to the reaction of the organosilane with oxygen-containing compounds.

The internal surface of the container, or the surface to be treated, may be subject to abrasion prior to reaction of the silicon-containing compound with oxygen-containing compounds in order to improve adhesion of the reaction product to the metal. Typical abrasion techniques may be found in copending non-provisional patent application Ser. No. 10/157,466, filed May 29, 2002, now published as U.S. 2003/0017359 A1.

The preferred vacuum baking step is typically, this is performed at a temperature of from about 30° C. to about 75° C., a duration of time of no less than 1 hour (preferably no less than 4 hours, even more preferably no less than 6 hours, and still more preferably no less than 12 hours), and a vacuum of no more than 100 torr (preferably no more than 1 torr and more preferably no more than 0.01 torr).

The internal metal surface is then subjected to the reaction between the silicon-containing compound and the oxygen-containing compound.

Silicon-containing compounds within the general formula (II) are known to react with oxygen-containing compounds, such as H₂O, N₂O, CO₂, and the like, to produce SiO₂, especially when the silicon-containing compounds are in the gaseous or vapor state. SiR¹R²R³R⁴  (II) This fact is taken advantage of in the practice of the various aspects of the invention. The reaction product of a silicon-containing compound and an oxygen-containing compound such as water forms an amorphous or crystalline glassy material on the surfaces on which it is deposited. The amorphous or crystalline glassy material may include aluminum silicide, if the container or surface being treated comprises aluminum. Although the deposited material is referred top herein as a “coating”, it shall be readily understood that in fact the material may deposit non-uniformly, or not at all on certain areas of the surface being treated. This coating then serves the function of deactivating a surface for the adsorption of molecules of the gas that is ultimately to be contained in the container or piping system at low concentration. In other words, the coating serves to decrease the number of reactive sites on the metal surface being treated. For simplicity, silicon-containing compounds within formula (II) shall be referred to as organosilanes, although their formal name under IUPAC convention may differ.

The reaction of an organosilane within general formula (II) with oxygen-containing materials such as water proceeds without catalyst at room temperature (25° C.); however, it is preferred to carry out the reaction at moderately elevated temperatures, such as temperature ranging from 25° C. up to 100° C., in order to produce the coatings in reasonable time. Most preferably, the temperature is maintained at not more than 74° C. The pressure of the reaction of an organosilane with water vapor will generally also proceed at atmospheric pressure, however, the pressure in the container, or near the surface being treated, may either be in vacuum or above atmospheric pressure. This will of course depend on the rates of reaction of the organosilane with the oxygen-containing compound, the desired coating deposition rate, and desired thickness of the coating. It is of course within the invention to make layered coatings of two or more organosilane/oxygen-containing compound reaction products. It is also considered within the invention to employ two or more organosilanes simultaneously to make a “mixed” coating. Indeed, it is possible that the organosilane may be employed in conjunction with a non-organosilane to form either layered or mixed coatings.

Silane and organosilanes are toxic materials, and, depending on the organosilane, pyrophoric. Special care in handling these materials is warranted, preferably well-ventilated hoods. Electronic grade silane (SiH₄) is available commercially in cylinders from Air Liquide America Corporation, Houston, Tex. Trimethylsilane is available commercially from Dow Corning Corporation.

Preferred silicon-containing compounds include silane, and methyl-containing organosilanes; particularly those wherein the methyl-containing organosilane is selected from the group consisting of methylsilane, dimethylsilane, trimethylsilane and tetramethylsilane. Preferred organosilane compounds include methylsilane compounds having the structure SiH_(n)(CH₃)_(4-n), where n=1 to 3, i.e. methylsilane, dimethylsilane, or trimethylsilane or the structure Si₂H_(m)(CH₃)_(6-m), where m=1 to 5. The most preferred organosilane compound is methylsilane, CH₃SiH₃. The organosilane compounds are hydrolyzed by reaction with water, oxygen or water-containing gases such as humid air and/or other oxygen-containing gases, such that the carbon content of the deposited film is from 1 to 50% by atomic weight, preferably about 20%.

It is conceivable to employ adjuvants during the reaction of an organosilane with water. In the practice of the invention, “adjuvant” includes physical and chemical adjuvants, and combinations thereof. Suitable physical adjuvants include electrostatic discharge, plasma discharge, laser excitation, and the like, under temperatures and pressures suitable for each of these processes. For example, plasmas are preferably best employed in moderate vacuum. A chemical adjuvant might include an oxidant gas such as oxygen, ozone, chlorine dioxide, combinations thereof, and the like. When a combination of physical and chemical adjuvants is employed, for example ozone and plasma discharge, the reaction product may be described as similar to the films produced b the process described in U.S. Pat. No. 6,054,379, which is incorporated herein by reference for its teaching of the production of such films.

Preferably, the silicon-containing composition is %1 Silane in N₂ and is maintained at 100 psig for 1 day during which it reacts with any oxygen-containing compounds present, such as moisture or air.

The container or surface to be treated may be selected from the group consisting of iron, stainless steel (for example 301, 316, 401), aluminum, aluminum alloy, steel alloys and the like.

Once the metal container inner surface, or metal surface to be treated, is cleaned, and the reaction of organosilane with oxygen-containing compounds completed (either with or with out adjuvants) to form a coating, the processes of the invention include evacuating the container for a time and vacuum sufficient to remove substantially all silicon-containing compound(s) that has not reacted with oxygen-containing compounds. This first evacuation step preferably includes evacuation down to a vacuum of about 1 torr, more preferably down to 0.01 torr. The temperature during this evacuation process is not critical, but higher temperatures may tend to increase the removal rate of organosilane. This will be balanced by safety issues, in that higher temperatures may be more hazardous. Therefore, room temperature (about 25° C.), or slightly lower or slightly higher than room temperature is preferred. After the vacuum step is performed, it is followed by a N2 fill step.

Subsequent to this first evacuation step, the next step is exposing the coating to a gas composition, the gas composition having a concentration of an acid gas that is greater than an intended acid gas concentration of a manufactured product. The acid gas is caused to contact the coating and deactivate the surface even further. The acid gas preferably has a concentration of at least 10 times the concentration of the acid gas that is to be stored in the container or exposed to the surface, more preferably has a concentration 50 times greater than the concentration of the acid gas that is to be stored in the container, still more preferably 500 times greater than the ultimate concentration, and even still more preferably 50,000 times the concentration of the acid gas to be stored in the container. When H₂S is selected as the acid gas, it is preferred to perform this step using 5000 ppm H₂S in N₂ at 100 psig.

Typical acid gases in include carbon disulfide, carbonylsulfide, and compounds within formula (I): Y—S—X  (I) wherein S is sulfur, X and Y are the same or different and are independently selected from the group of hydrogen, alkyl, aryl, oxygen, hydoxyl, amine, aminosilane, oxygen, and alcohol.

Examples of preferred sulfur-containing compounds within formula (I) include hydrogen sulfide, carbonyl sulfide, sulfur dioxide, methylthiol, ethylthiol, n-propylthiol, i-propylthiol, benzylthiol, and the like. Especially preferred sulfur-containing compunds within formula (I) include hydrogen sulfide, carbonyl sulfide and sulfur dioxide.

The degree of adsorption of the acid gas onto the coating depends in a complicated way on the composition and physical properties of the coating, the temperature and pressure employed during this step, as well as on the chemical and physical properties of the particular acid gas that is being adsorbed thereon. These parameters are in turn dictated by the final concentration of acid gas that is to be stored in the container. A discussion of adsorption of gaseous species onto surfaces that is helpful in this respect is included in Daniels, F. et al., “Experimental Physical Chemistry”, Seventh Edition, McGraw-Hill, pages 369-374 (1970). While the inventors are not certain, it is believed that the attraction of the acid gas to the coating is physical in nature, involving an interaction of dipoles or induced dipoles, but may be chemical in nature involving chemical bonds, as when oxygen is adsorbed on charcoal. A combination of physical and chemical forces may be at work as well. Thus, the surface area of a coating produced by the practice of the present invention may be determined by the B.E.T. method, and preferably is at least about 1 m²/gram, more preferably at least 10 m²/gram. If the coating is somewhat porous, the pore volume may be determined by nitrogen adsorption isotherm methods, and is preferably at least 0.1 ml/gram. The B.E.T. method is described in detail in Brunauer, S. Emmet, P. H., and Teller, E., J. Am. Chem. Soc., 60, 309-16 (1938). The nitrogen adsorption isotherm method is described in detail in Barrett, E. P., Joyner, L. G. and Helenda, P. P., J. Am. Chem. Soc., 73, 373-80 (1951), incorporated by reference herein. In general, if the concentration of acid gas to be stored in the container is 100 ppb, then for the same acid gas, same temperature and pressure, and same coating, the concentration of acid gas used in this step will be higher than if the ultimate concentration of acid gas is to be only 50 ppb, assuming adsorption is the governing pathway. An increase in temperature will tend to require an increase in concentration of acid gas, an increase in pressure, or both, to achieve the same degree of adsorption. In contrast, a decrease in temperature will tend to require a decreased concentration of acid gas, a decrease in pressure, or both to achieve the same level of adsorption.

After the surface has been further deactivated by exposure to the acid gas at high concentration, a second evacuation step is carried out to remove excess acid gas. In this step, evacuation of the container is carried out for a time sufficient to remove substantially all of non-adsorbed acid gas, leaving acid gas adsorbed on the coating. Once the metal container inner surface, or metal surface to be treated, is cleaned, and the reaction of organosilane with oxygen-containing compounds completed (either with or with out adjuvants) to form a coating, the processes of the invention include evacuating the container for a time and vacuum sufficient to remove substantially all silicon-containing compound(s) that has not reacted with oxygen-containing compounds. Preferably, this step is performed down to a vacuum of about 1 torr, more preferably down to 0.01 torr. The temperature during this evacuation process is not critical, but higher temperatures may tend to increase the removal rate of organosilane. This will be balanced by safety issues, in that higher temperatures may be more hazardous. Therefore, room temperature (about 25° C.), or slightly lower or slightly higher than room temperature is preferred. After the vacuum step is performed, it is followed by a N2 fill step.

When SO₂ is selected as the acid gas, steps in addition to the foreoing are preferable and include the following. After completion of the reaction between the silicon-containing and oxygen-containing compounds, but before the vacuum and N2 fill step, the cylinder is subjected to five cycles of being filled with Nitrogen at 100 psi followed by venting. Similarly, after completion of the exposure of the internal cylinder surface to SO₂ (the selected acid gas), but before the vacuum and N2 fill step, the treated cylinder is again subjected to five cycles of being filled with Nitrogen at 100 psi followed by venting.

The container is then filled with a gas composition comprising the intended low concentration of acid gas in the balance gas. While preferred manufactured products of the invention comprise only a single acid gas with one balance gas, two or more acid gases and/or two or more balance gases may be used. Typical balance gases include noble gases, nitrogen, ethylene, propylene, and mixtures thereof.

As shown below in the Examples, application of the method of the invention to acid gases having concentrations below 500 ppb exhibits unexpectedly good stability. The unexpected stability is even more surprising as the concentration utilized ranges from about 50 ppb to about 100 ppb.

EXAMPLES

In the following examples, hydrogen sulfide concentrations were measured using a chemluminescence detector.

Examples 1-3

In order to betatest the process of the invention in a production environment, a betatest was performed at a specialty gas fill plant located in Santa Fe Springs, Calif. All cylinders were kept and analyzed on site for approximately one month and then transferred to a laboratory and maintained there for further analysis.

Each of the cylinders were treated as follows:

Step 1 (Vacuum Bake): Cylinders go through a vacuum/fill bake cycle for a minimum of 4 hours

Step 2 (Silane Passivation): Cylinders attached to manifold and vacuumed. Cylinders filled with 1% Silane in N₂ to 100 psig and maintained for 1 day. Manifold vented and vacuumed.

Step 3 (Silane Removal and H₂S Passivation): Cylinders attached to manifold and vented. Cylinders go through a vacuum/N₂ fill cycle. Vacuumed cylinders filled with 5000 ppm H₂S in N₂ to 100 psig and maintained for 4 days. Manifold vented through a scrubber and vacuumed.

Step 4 (H₂S Removal): Cylinders attached to manifold and vented out through scrubber. Cylinders go through a vacuum/N₂ fill cycle. Cylinders vacuumed for at least 2 hours.

Step 5 (Standard Filling): Cylinders filled to target concentration from a 10 ppm mother mixture in Nitrogen. TABLE 1 Cylinder Size and Fill Concentration H₂S Fill Concentration Example Cylinder # Size (ppb) 1 42553 16 53.1 2 144244 30 48.5 3 144270 30 96.9

TABLE 2 H₂S Concentration Over Time for Examples 1-3 Example 1: Example 2: Example 3: Cyl. # 42553 Cyl. # 144244 Cyl. # 144270 days ppb H₂S days ppb H₂S days ppb H₂S 0 53.1 0 48.5 0 96.9 1 62 1 46.1 1 99 19 39.9 20 48.1 20 90.7 77 43.5 78 46.51 78 101.57 110 43.9 132 50.8 132 100.5 188 46.2 201 55.8 201 97.3 231 45.1 230 53.6 230 102.2 277 45.3 277 49.4 277 103.6 532 39.3 329 44.8 329 92.5 691 33.2 532 44.9 532 95 691 33.9 691 81.1 As best illustrated in FIG. 1, the H₂S concentration for Examples 1-3 is stable over an approximate 700 day period of time.

Examples 4-7 and Comparative Examples 1-7

Examples 4-7 were prepared as follows:

Step 1 (Vacuum Bake): Cylinders go through a vacuum/fill bake cycle for a minimum of 4 hours

Step 2 (Silane Passivation): Cylinders attached to manifold and vacuumed. Cylinders filled with 1% Silane in N₂ to 100 psig and maintained for the time indicated in Table 3. Manifold vented and vacuumed.

Step 3 (Silane Removal and H₂S Passivation): Cylinders attached to manifold and vented. Cylinders go through a vacuum/N₂ fill cycle. Vacuumed cylinders filled with 5000 ppm H₂S in N₂ to 100 psig and maintained for the time indicated in Table 3. Manifold vented through a scrubber and vacuumed.

Step 4 (H₂S Removal): Cylinders attached to manifold and vented out through scrubber. Cylinders go through a vacuum/N₂ fill cycle. Cylinders vacuumed for at least 2 hours.

Step 5 (Standard Filling): Cylinders filled to target concentration from a 10 ppm mother mixture in Nitrogen.

Comparative Examples 1-3 and 7 were prepared as follows:

Step 1 (Vacuum Bake): Cylinders go through a vacuum/fill bake cycle for a minimum of 4 hours

Step 2 (Silane Passivation): Cylinders attached to manifold and vacuumed. Cylinders filled with 1% Silane in N₂ to 100 psig and maintained for the time indicated in Table 3. Manifold vented and vacuumed.

Step 3 (Silane Remova): Cylinders attached to manifold and vented. Cylinders go through a vacuum/N₂ fill cycle. Cylinders vacuumed for at least 2 hours.

Comparative Examples 4-6 were prepared as follows:

Step 1 (Vacuum Bake): Cylinders go through a vacuum/fill bake cycle for a minimum of 4 hours

Step 2 (H₂S Passivation): Cylinders filled with 5000 ppm H₂S in N₂ to 100 psig and maintained for the time indicated in Table 3. Manifold vented through a scrubber and vacuumed.

Step 3 (H₂S Removal): Cylinders attached to manifold and vented out through scrubber. Cylinders go through a vacuum/N₂ fill cycle. Cylinders vacuumed for at least 2 hours.

Step 4 (Standard Filling): Cylinders filled to target concentration from a 10 ppm mother mixture in Nitrogen. TABLE 3 Cylinder Size, Silane and H₂S Passivation Periods, and Fill Concentrations H₂S Fill Cylinder Silane conc. Cylinder # Size (days) H₂S (days) (ppb) Comp. Ex. 1 24271 Size 7 94 0 101.2 Comp. Ex. 2 24283 Size 7 29 0 101.2 Comp. Ex. 3 24287 Size 7 96 0 101.2 Comp. Ex. 4 24235 Size 7 0 42 101.2 Comp. Ex. 5 24305 Size 7 0 39 105.0 Comp. Ex. 6 24313 Size 7 0 39 105.0 Ex. 4 24335 Size 7 35 14 105.0 Comp. Ex. 7 15042 Size 30 61 0 76.4 Ex. 5 15031 Size 30 27 30 104.0 Ex. 6 15035 Size 30 27 30 104.0 Ex. 7 15039 Size 30 8 57 76.4

TABLE 4 H₂S Concentration Over Time for Comparative Examples 1-6 Comp. Ex. Comp. Ex. Comp. Ex. Comp. Ex. Comp. Ex. Comp. Ex. 1: Cyl. # 2: Cyl. # 3: Cyl. # 4: Cyl. # 5: Cyl. # 6: Cyl. # 24271 24283 24287 24235 24305 24313 ppb ppb ppb ppb ppb ppb days H₂S days H₂S days H₂S days H₂S days H₂S days H₂S 0 101.2 0 101.2 0 101.2 0 101.2 0 90 0 91 8 102.6 8 91.7 8 108.8 1 86.37 2 91.7 2 97.5 15 77.34 15 82 15 73.8 5 90.7 6 87 6 97.2 23 92.1 23 58 23 81.3 6 84.9 28 81.67 28 97 43 80.6 43 47.6 43 73.1 7 92.4 45 79.1 45 97.1 49 69.9 49 42.5 49 66.1 9 87.3 49 74 49 81.8 74 81.3 74 76.3 13 84.3 57 68.2 57 94.1 101 76.7 101 67.7 14 87.1 77 60.1 77 86.6 150 75 150 69 22 93 83 58.7 83 81.2 239 72.2 163 63.4 33 83.2 108 71.2 108 100.7 296 61.8 239 64.8 36 95.4 135 67.2 135 101.8 319 65.7 296 52 40 100.8 184 66.3 184 99.1 490 36.2 319 59.1 61 89.1 197 62.2 197 100.8 490 21.7 78 84.3 273 56.9 273 101.8 81 82.4 524 13.9 330 96.3 89 84.6 524 65.5 109 76.4 665 48.4 115 74.53 140 86.9 167 83.2 216 87.3 229 80.3 362 69.7 385 66.4 447 59.6

TABLE 5 H₂S Concentration Over Time for Examples 4-7 & Comparative Example 7 24335 15031 15035 15039 15042 ppb ppb ppb ppb ppb days H₂S days H₂S days H₂S days H₂S days H₂S 0 87 0 104 0 104 0 76.4 0 76.4 2 97.7 9 108.8 9 108.9 1 79.4 1 74.2 6 101 15 97.2 15 96 8 65.4 8 61.4 28 105.5 23 96.8 23 100.5 9 72.8 9 59.2 45 96.4 43 91.2 43 97 29 73 29 52.1 49 99.4 44 103.6 44 112.6 30 71.6 30 55.3 57 100.2 49 86 49 89.2 35 66.6 35 50.5 77 87 50 93 50 98.8 36 73.1 36 48.3 83 90.2 52 100.7 52 102 38 76.6 38 51.5 108 103.1 67 96.1 67 100 44 70.6 53 39.5 135 105.2 74 92.2 74 95.1 53 73.5 60 39.7 184 109.1 91 90.2 91 92.9 60 73 77 38.3 197 103.9 92 94 92 95 77 65 78 41.9 273 109.9 114 91.1 114 93.7 78 71.1 100 36.3 330 108 127 95.7 127 102.6 100 72.2 113 41.9 353 131.2 150 102.4 150 102.2 113 78.4 136 40 415 123.3 183 97.8 183 94.3 136 78.1 169 35.4 518 114.1 238 97.6 238 103.9 169 73.2 224 33.8 562 112.3 287 93.8 284 93.9 224 79.5 270 25.1 660 104.4 381 99.6 381 111.8 270 70.1 451 0 867 109.3 491 84.7 429 98.3 367 76.4 1023 102 574 93.9 497 95.2 477 70.8 626 78 574 107.2 560 74.1 829 86.7 626 93.9 612 65 989 78.2 829 100.8 815 70.2 989 87.3 975 63.3

As best shown in FIG. 2, Example 4 in comparison to only Silane passivation or only H₂S passivation (for the same size cylinder) exhibited excellent stability.

As best shown in FIG. 3, Examples 5-7 in comparison to only Silane passivation (for the same size cylinder) exhibited excellent stability.

Example 8

In an effort to study the effect of reducing production time to less than two weeks for low-level COS/H₂S in Nitrogen mixtures, the passivation times were shortened. A cylinder used for the COS/H₂S mixture underwent the following treatment:

Example 8 was prepared as follows:

Step 1 (Vacuum Bake): Size 16 cylinder goes through a vacuum/fill bake cycle for a minimum of 4 hours

Step 2 (Silane Passivation): Cylinder attached to manifold and vacuumed. Cylinder filled with 1% Silane in N₂ to 100 psig and maintained for 3 days. Manifold vented and vacuumed.

Step 3 (Silane Removal and H₂S Passivation): Cylinder attached to manifold and vented. Cylinder goes through a vacuum/N₂ fill cycle. Vacuumed cylinders filled with 5000 ppm H₂S in N₂ to 100 psig and maintained for 8 days. Manifold vented through a scrubber and vacuumed.

Step 4 (H₂S Removal): Cylinder attached to manifold and vented out through scrubber. Cylinder goes through a vacuum/N₂ fill cycle. Cylinder vacuumed for at least 2 hours.

Step 5 (Standard Filling): Cylinder filled to a concentration 52.1 ppb COS and 49.7 ppb H₂S in Nitrogen. TABLE 6 H₂S and COS Concentrations Over Time for Example 8 Example 8: Cylinder # 42589 days ppb H₂S ppb COS 0 49.7 52.1 2 59.9 52.4 32 50 64.4 38 57.9 69.9 114 57 55.5 197 48.6 56.1 401 50.3 58.3 576 56.2 48.7

As best shown in FIG. 4, Example 8 exhibited excellent stability.

Examples 9-11

The invention was also tested for H₂S and COS mixtures in balance Ethylene at approximate concentrations of about 100 ppb. Two Ethylene grades were tested as the balance gas: 99.95% (CP grade) and 99.9995% (5N5 grade).

Example 9 was prepared as follows.

Step 1 (Vacuum Bake): Size 7 cylinder goes through a vacuum/fill bake cycle for a minimum of 4 hours

Step 2 (Silane Passivation): Cylinder attached to manifold and vacuumed. Cylinder filled with 1% Silane in N₂ to 100 psig and maintained for 4 days. Manifold vented and vacuumed.

Step 3 (Silane Removal and H₂S Passivation): Cylinder attached to manifold and vented. Cylinder goes through a vacuum/N₂ fill cycle. Vacuumed cylinders filled with 5000 ppm H₂S in N₂ to 100 psig and maintained for 4 days. Manifold vented through a scrubber and vacuumed.

Step 4 (H₂S Removal): Cylinder attached to manifold and vented out through scrubber. Cylinder goes through a vacuum/N₂ fill cycle. Cylinder vacuumed for at least 2 hours.

Step 5 (Standard Filling): Filled with 106 ppb COS in 5N5 Ethylene.

Example 10 was prepared as follows:

Step 1 (Vacuum Bake): Size 16 cylinder goes through a vacuum/fill bake cycle for a minimum of 4 hours

Step 2 (Silane Passivation): Cylinder attached to manifold and vacuumed. Cylinder filled with 1% Silane in N₂ to 100 psig and maintained for 3 days. Manifold vented and vacuumed.

Step 3 (Silane Removal and H₂S Passivation): Cylinder attached to manifold and vented. Cylinder goes through a vacuum/N₂ fill cycle. Vacuumed cylinders filled with 5000 ppm H₂S in N₂ to 100 psig and maintained for 9 days. Manifold vented through a scrubber and vacuumed.

Step 4 (H₂S Removal): Cylinder attached to manifold and vented out through scrubber. Cylinder goes through a vacuum/N₂ fill cycle. Cylinder vacuumed for at least 2 hours.

Step 5 (Standard Filling): Filled with 89.5 ppb H₂S in CP grade Ethylene.

Example 11 was prepared as follows:

Step 1 (Vacuum Bake): Size 16 cylinder goes through a vacuum/fill bake cycle for a minimum of 4 hours

Step 2 (Silane Passivation): Cylinder attached to manifold and vacuumed. Cylinder filled with 1% Silane in N₂ to 100 psig and maintained for 3 days. Manifold vented and vacuumed.

Step 3 (Silane Removal and H₂S Passivation): Cylinder attached to manifold and vented. Cylinder goes through a vacuum/N₂ fill cycle. Vacuumed cylinders filled with 5000 ppm H₂S in N₂ to 100 psig and maintained for 8 days. Manifold vented through a scrubber and vacuumed.

Step 4 (H₂S Removal): Cylinder attached to manifold and vented out through scrubber. Cylinder goes through a vacuum/N₂ fill cycle. Cylinder vacuumed for at least 2 hours.

Step 5 (Standard Filling): Filled with 98.8 ppb COS in CP grade Ethylene. TABLE 7 H₂S and COS Concentrations Over Time for Examples 9-11 Example 9: Example 10: Example 11: Cylinder # 27525 Cylinder # 42573 Cylinder # 42543 days ppb COS days ppb H₂S days ppb COS 0 106 0 89.5 0 98.8 1 131.9 2 81.4 2 80.4 7 76.4 32 111.3 38 120.6 23 94.7 38 124.9 112 119.4 55 109 112 105.7 133 109.7 142 113.4 130 95 198 98.9 216 108.6 193 95.8 401 84.3 237 82.8 366 85.9 576 100.5 302 89.7 401 88.3 680 78.6 576 76.7

As best shown in FIG. 5, Example 9-11 exhibited excellent stability.

Examples 12-13

The cylinder treatment of the invention was performed with an extra step where the cylinder was filled with Nitrogen at 100 psi and vented five times after each passivation with Silane and each passivation with SO₂.

Examples 12-13 were prepared as follows:

Step 1 (Vacuum Bake): Cylinder goes through a vacuum/fill bake cycle for a minimum of 4 hours

Step 2 (Silane Passivation): Cylinder attached to manifold and vacuumed. Cylinder filled with 1% Silane in N₂ to 100 psig and maintained for 43 days.

Step 3 (Silane Removal and SO₂ Passivation): Manifold vented and filled with N2 at 100 psig. This was repeated 4 times. Cylinder goes through a vacuum/N₂ fill cycle. Vacuumed cylinders filled with 500 ppm SO₂ in N₂ to 100 psig and maintained for 8 days. Manifold vented through a scrubber and vacuumed.

Step 4 (SO₂ Removal): Cylinder attached to manifold vented and filled with N2 at 100 psig. This was repeated 4 times. They were vacuumed and then filled with 100 psi of pure Propylene for 7 days. Cylinder attached to manifold vented and filled with N2 at 100 psig. This was repeated 4 times. Cylinder vacuumed for at least 2 hours.

Step 5 (Standard Filling): Filled with 100 ppb SO₂ in Propylene at 100 psi. TABLE 8 SO₂ Concentration Over Time for Examples 12-13 Example 12: Example 13: Cylinder # 6513 Cylinder # 6514 days ppb SO₂ days ppb SO₂ 0 100 0 100 14 71 14 93 28 113 28 101 42 73 42 110 56 88 56 142 70 104 70 129 100 102 100 129 130 112 130 127 170 108 170 140 210 105 210 114 260 98 260 113 300 97 300 111

As best shown in FIG. 6, Example 12-13 exhibited excellent stability.

Examples 14-17 and Comparative Example 8

Examples 14-17 and Comparative Example 8 were prepared as follows:

Step 1 (Vacuum Brake): Cylinders go through a vacuum/fill bake cycle.

Step 2 (Silane Passivation): Cylinders attached to manifold and vacuumed. Cylinders filled with 1% Silane in N₂ to 100 psig and maintained for the period indicated in Table 9. Manifold vented and vacuumed.

Step 3 (Silane Removal and H₂S Passivation): Cylinders attached to manifold and vented. Cylinders go through a vacuum/N₂ fill cycle. Vacuumed cylinders filled with 5000 ppm H₂S in N₂ to 100 psig and maintained for the period indicated in Table 9. Manifold vented through a scrubber and vacuumed.

Step 4 (H₂S Removal): Cylinders attached to manifold and vented out through scrubber. Cylinders go through a vacuum/N₂ fill cycle. TABLE 9 Passivation Times for Ex. 14-17 and Comp. Ex. 8 Silane Passivation H₂S Passivation (days) (days) H₂S (ppb) Example 14 1 1 109.3 Example 15 1 2 109.3 Example 16 1 3 110.6 Example 17 1 4 96.9 Comparative 4 0 110.6 Example 8

TABLE 10 H₂S Concentration Over Time for Ex. 14-15 and Comp. Ex. 8 Comp. Ex. 8 Ex. 14 Ex. 15 days H₂S (ppb) days H₂S (ppb) days H₂S (ppb) 0 110.6 0 109.3 0 109.3 1 104.3 2 116.8 1 117.5 2 89.2 10 106.8 2 118.6 10 65 23 97 10 102.7 23 46.1 29 100.8 23 93.3 29 42.2 36 111.6 29 91.1 36 45.3 42 97.6 36 104 42 30.9 57 101.9 42 85.8 65 88.5 57 84.2 79 71.6 65 74.7 205 38.9 79 58.1 115 38.5

TABLE 11 H₂S Concentration Over Time for Ex. 16-17 Ex. 16 Ex. 17 days H₂S (ppb) days H₂S (ppb) 0 110.6 0 96.9 1 113.7 1 99 2 119.2 20 90.7 10 110.7 78 101.6 23 108.1 132 100.5 29 113.2 201 97.3 36 123.6 230 102.2 42 114 277 103.6 57 124.3 329 92.5 65 116.1 79 88.9 115 92.7 269 80.9 414 61.2

As best shown in FIG. 7, increasing the H₂S passivation time improved stability.

Although the description herein is intended to be representative of the invention, it is not intended to limit the scope of the appended claims. 

1. An article of manufacture comprising: a) a container having an internal space and a passivated internal metal surface; and b) a composition comprising an acid gas and a balance gas contained within the internal space and in contact with the passivated internal metal surface; wherein i) the acid gas has an intended concentration in the balance gas of less than 500 ppb; ii) the acid gas is selected from the group consisting of carbon, disulfide, carbonylsulfide, and compounds within the formula Y—S—X  wherein S is sulfur, X and Y are the same or different and are independently selected from the group consisting of hydrogen, alkyl, aryl, oxygen, hydoxyl, amine, aminosilane, oxygen, and alcohol; and iii) the passivated internal metal surface comprises A) the reaction product of a silicon-containing material and an oxygen-containing material, and B) an amount of the acid gas adsorbed on or in the passivated internal metal surface which is effective to enhance the stability of the intended concentration over time.
 2. The article of manufacture of claim 1, wherein the acid gas is selected from the group consisting of hydrogen sulfide, carbonyl sulfide, sulfur dioxide, methylthiol, ethylthiol, n-propylthiol, i-propylthiol, and benzylthiol.
 3. The article of manufacture of claim 1, wherein the acid gas is selected from the group consisting of hydrogen sulfide, carbonyl sulfide, and sulfur dioxide.
 4. The article of manufacture of claim 1, wherein the silicon-containing material is selected from the group consisting of compounds within the general formula (II): SiR¹R²R³R⁴  (II) wherein R1, R2, R3, and R4 are the same or different and are independently selected from the group consisting of hydrogen, halogen, amine, alkyl, aryl, halogenated alkyl, and halogenated aryl.
 5. The article of manufacture of claim 1, wherein the oxygen-containing compound is selected from the group consisting of moisture, molecular oxygen, metal oxides, and mixtures thereof.
 6. The article of manufacture of claim 1, wherein the silicon-containing compound is silane.
 7. The article of manufacture of claim 1, wherein the silicon-containing compound is a methyl-containing silane selected from the group consisting of methylsilane, dimethylsilane, trimethylsilane and tetramethylsilane.
 8. The article of manufacture of claim 1, wherein the acid gas contained within the internal space has a concentration of about 50-100 ppb.
 9. The article of manufacture of claim 8, wherein the acid gas is hydrogen sulfide.
 10. The article of manufacture of claim 8, wherein the acid gas is carbonyl sulfide.
 11. The article of manufacture of claim 8, wherein the acid gas is sulfur dioxide.
 12. The article of manufacture of claim 1, wherin the balance gas is selected from the group consisting of noble gases, nitrogen, ethylene, propylene, and mixtures thereof.
 13. A method of producing the article of manufacture of claim 1, comprising the steps of: exposing an internal metal surface of a container to a first composition comprising at least one silicon-containing compound for a time sufficient to allow at least some of the at least one silicon-containing compound to react with oxygen-containing compounds present to form a silicon-treated surface on at least some of the internal metal surface, the silicon-containing compound selected from the group consisting of compounds within the general formula (II): SiR¹R²R³R⁴  (II) wherein R1, R2, R3, and R4 are the same or different and are independently selected from the group consisting of hydrogen, halogen, alkyl, aryl, amine, halogenated alkyl, and halogenated aryl; evacuating the container for a time sufficient to remove substantially all of the at least one silicon-containing compound that has not reacted with the oxygen-containing compound to form the silicon-treated surface; exposing the silicon-treated surface to a second composition comprising the acid gas having a concentration that is greater than an intended concentration of the acid gas contained within the internal space; evacuating the container for a time sufficient to remove an amount of the second composition to enhance the stability of the intended concentration over time; and filling the container with a third composition comprising the acid gas at the intended concentration.
 14. The method of claim 13, further comprising the step of exposing the internal metal surface to vacuum at a temperature greater than ambient before said step of exposing an internal metal surface of a container to a first composition.
 15. The method of claim 13, wherein the time in which the internal metal surface is exposed to the first composition is no less than 1 day.
 16. The method of claim 13, wherein the silicon-treated surface is exposed to the second composition for a period of time of at least 1 day.
 17. The method of claim 13, wherein the silicon-treated surface is exposed to the second composition for a period of time of from about 1 day to about 4 days.
 18. A method of calibrating a measurement device for measuring a concentration of an acid gas, the method comprising the steps of: providing the article of manufacture of claim 1; using a portion of the acid gas contained within the manufactured product in a calibration of the measurement device; and repeating said step of using a portion at least once, wherein a period of time commencing from a first performance of said step of using a portion and expiring on a later repetition of said step of using a portion is not less than 30 days.
 19. The method of claim 18, wherein the period of time is not less than 90 days.
 20. The method of claim 18, wherein the period of time is not less than 180 days.
 21. The method of claim 18, wherein the period of time is not less than 12 months.
 22. The method of claim 18, wherein the period of time is not less than 18 months. 